A study of the adsorption of methyl radicals on clean and oxygen-modified Ni(100)

Karen A. Dickens, Peter C Stair

Research output: Contribution to journalArticle

29 Citations (Scopus)

Abstract

The adsorption of methyl radicals has been studied by X-ray photoelectron spectroscopy and temperature-programmed desorption (TPD) on a clean Ni(100) surface, Ni(100) with a chemisorbed oxygen overlayer, and Ni(100) with a NiO(111) oxide overlayer. Methyl radical dosing at surface temperatures of 120-170 K produces carbon coverages in excess of 5 monolayers with a C(1s) peak position indicative of an adsorbed hydrocarbon species. The carbon coverage never saturated on any of surfaces studied. TPD indicating C2-C4 formation was observed following very large methyl radical exposures. These results are indicative of the formation of surface hydrocarbon chains. The methyl radical gas temperature had no effect on the surface chemistry. However, hydrocarbon chains formed with higher selectivity on the oxygen-modified surfaces compared to the clean surface. These results suggest that a direct reaction between incoming methyl radicals and adsorbed hydrocarbon groups is not involved. The chains are likely produced by polymerizaton of surface methylene species produced by dehydrogenation of chemisorbed methyl groups via a mechanism similar to the Fischer-Tropsch synthesis reaction. On NiO TPD results also indicate that surface alkoxy groups are formed based on the low-temperature desorption of CO.

Original languageEnglish
Pages (from-to)1444-1450
Number of pages7
JournalLangmuir
Volume14
Issue number6
Publication statusPublished - Mar 17 1998

Fingerprint

Oxygen
Adsorption
adsorption
oxygen
Hydrocarbons
Temperature programmed desorption
hydrocarbons
desorption
Carbon
Fischer-Tropsch synthesis
methyl radical
carbon
Dehydrogenation
Carbon Monoxide
dehydrogenation
gas temperature
Surface chemistry
methylene
Temperature
Oxides

ASJC Scopus subject areas

  • Colloid and Surface Chemistry
  • Physical and Theoretical Chemistry

Cite this

A study of the adsorption of methyl radicals on clean and oxygen-modified Ni(100). / Dickens, Karen A.; Stair, Peter C.

In: Langmuir, Vol. 14, No. 6, 17.03.1998, p. 1444-1450.

Research output: Contribution to journalArticle

@article{67cbaed7a4f24b98b3af4b206f8bfccd,
title = "A study of the adsorption of methyl radicals on clean and oxygen-modified Ni(100)",
abstract = "The adsorption of methyl radicals has been studied by X-ray photoelectron spectroscopy and temperature-programmed desorption (TPD) on a clean Ni(100) surface, Ni(100) with a chemisorbed oxygen overlayer, and Ni(100) with a NiO(111) oxide overlayer. Methyl radical dosing at surface temperatures of 120-170 K produces carbon coverages in excess of 5 monolayers with a C(1s) peak position indicative of an adsorbed hydrocarbon species. The carbon coverage never saturated on any of surfaces studied. TPD indicating C2-C4 formation was observed following very large methyl radical exposures. These results are indicative of the formation of surface hydrocarbon chains. The methyl radical gas temperature had no effect on the surface chemistry. However, hydrocarbon chains formed with higher selectivity on the oxygen-modified surfaces compared to the clean surface. These results suggest that a direct reaction between incoming methyl radicals and adsorbed hydrocarbon groups is not involved. The chains are likely produced by polymerizaton of surface methylene species produced by dehydrogenation of chemisorbed methyl groups via a mechanism similar to the Fischer-Tropsch synthesis reaction. On NiO TPD results also indicate that surface alkoxy groups are formed based on the low-temperature desorption of CO.",
author = "Dickens, {Karen A.} and Stair, {Peter C}",
year = "1998",
month = "3",
day = "17",
language = "English",
volume = "14",
pages = "1444--1450",
journal = "Langmuir",
issn = "0743-7463",
publisher = "American Chemical Society",
number = "6",

}

TY - JOUR

T1 - A study of the adsorption of methyl radicals on clean and oxygen-modified Ni(100)

AU - Dickens, Karen A.

AU - Stair, Peter C

PY - 1998/3/17

Y1 - 1998/3/17

N2 - The adsorption of methyl radicals has been studied by X-ray photoelectron spectroscopy and temperature-programmed desorption (TPD) on a clean Ni(100) surface, Ni(100) with a chemisorbed oxygen overlayer, and Ni(100) with a NiO(111) oxide overlayer. Methyl radical dosing at surface temperatures of 120-170 K produces carbon coverages in excess of 5 monolayers with a C(1s) peak position indicative of an adsorbed hydrocarbon species. The carbon coverage never saturated on any of surfaces studied. TPD indicating C2-C4 formation was observed following very large methyl radical exposures. These results are indicative of the formation of surface hydrocarbon chains. The methyl radical gas temperature had no effect on the surface chemistry. However, hydrocarbon chains formed with higher selectivity on the oxygen-modified surfaces compared to the clean surface. These results suggest that a direct reaction between incoming methyl radicals and adsorbed hydrocarbon groups is not involved. The chains are likely produced by polymerizaton of surface methylene species produced by dehydrogenation of chemisorbed methyl groups via a mechanism similar to the Fischer-Tropsch synthesis reaction. On NiO TPD results also indicate that surface alkoxy groups are formed based on the low-temperature desorption of CO.

AB - The adsorption of methyl radicals has been studied by X-ray photoelectron spectroscopy and temperature-programmed desorption (TPD) on a clean Ni(100) surface, Ni(100) with a chemisorbed oxygen overlayer, and Ni(100) with a NiO(111) oxide overlayer. Methyl radical dosing at surface temperatures of 120-170 K produces carbon coverages in excess of 5 monolayers with a C(1s) peak position indicative of an adsorbed hydrocarbon species. The carbon coverage never saturated on any of surfaces studied. TPD indicating C2-C4 formation was observed following very large methyl radical exposures. These results are indicative of the formation of surface hydrocarbon chains. The methyl radical gas temperature had no effect on the surface chemistry. However, hydrocarbon chains formed with higher selectivity on the oxygen-modified surfaces compared to the clean surface. These results suggest that a direct reaction between incoming methyl radicals and adsorbed hydrocarbon groups is not involved. The chains are likely produced by polymerizaton of surface methylene species produced by dehydrogenation of chemisorbed methyl groups via a mechanism similar to the Fischer-Tropsch synthesis reaction. On NiO TPD results also indicate that surface alkoxy groups are formed based on the low-temperature desorption of CO.

UR - http://www.scopus.com/inward/record.url?scp=0032027306&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0032027306&partnerID=8YFLogxK

M3 - Article

VL - 14

SP - 1444

EP - 1450

JO - Langmuir

JF - Langmuir

SN - 0743-7463

IS - 6

ER -