Defect creation by linker fragmentation in metal-organic frameworks and its effects on gas uptake properties

Gokhan Barin, Vaiva Krungleviciute, Oleksii Gutov, Joseph T Hupp, Taner Yildirim, Omar K. Farha

Research output: Contribution to journalArticle

62 Citations (Scopus)

Abstract

We successfully demonstrate an approach based on linker fragmentation to create defects and tune the pore volumes and surface areas of two metal-organic frameworks, NU-125 and HKUST-1, both of which feature copper paddlewheel nodes. Depending on the linker fragment composition, the defect can be either a vacant site or a functional group that the original linker does not have. In the first case, we show that both surface area and pore volume increase, while in the second case they decrease. The effect of defects on the high-pressure gas uptake is also studied over a large temperature and pressure range for different gases. We found that despite an increase in pore volume and surface area in structures with vacant sites, the absolute adsorption for methane decreases for HKUST-1 and slightly increases for NU-125. However, the working capacity (deliverable amount between 65 and 5 bar) in both cases remains similar to parent frameworks due to lower uptakes at low pressures. In the case of NU-125, the effect of defects became more pronounced at lower temperatures, reflecting the greater surface areas and pore volumes of the altered forms.

Original languageEnglish
Pages (from-to)6914-6919
Number of pages6
JournalInorganic Chemistry
Volume53
Issue number13
DOIs
Publication statusPublished - Jul 7 2014

Fingerprint

fragmentation
Gases
Metals
porosity
Defects
defects
gases
metals
Methane
Functional groups
Copper
methane
low pressure
fragments
Adsorption
copper
Temperature
adsorption
Chemical analysis
temperature

ASJC Scopus subject areas

  • Inorganic Chemistry
  • Physical and Theoretical Chemistry

Cite this

Defect creation by linker fragmentation in metal-organic frameworks and its effects on gas uptake properties. / Barin, Gokhan; Krungleviciute, Vaiva; Gutov, Oleksii; Hupp, Joseph T; Yildirim, Taner; Farha, Omar K.

In: Inorganic Chemistry, Vol. 53, No. 13, 07.07.2014, p. 6914-6919.

Research output: Contribution to journalArticle

Barin, Gokhan ; Krungleviciute, Vaiva ; Gutov, Oleksii ; Hupp, Joseph T ; Yildirim, Taner ; Farha, Omar K. / Defect creation by linker fragmentation in metal-organic frameworks and its effects on gas uptake properties. In: Inorganic Chemistry. 2014 ; Vol. 53, No. 13. pp. 6914-6919.
@article{2baaabc1a8944673b0d748eeb3c6a723,
title = "Defect creation by linker fragmentation in metal-organic frameworks and its effects on gas uptake properties",
abstract = "We successfully demonstrate an approach based on linker fragmentation to create defects and tune the pore volumes and surface areas of two metal-organic frameworks, NU-125 and HKUST-1, both of which feature copper paddlewheel nodes. Depending on the linker fragment composition, the defect can be either a vacant site or a functional group that the original linker does not have. In the first case, we show that both surface area and pore volume increase, while in the second case they decrease. The effect of defects on the high-pressure gas uptake is also studied over a large temperature and pressure range for different gases. We found that despite an increase in pore volume and surface area in structures with vacant sites, the absolute adsorption for methane decreases for HKUST-1 and slightly increases for NU-125. However, the working capacity (deliverable amount between 65 and 5 bar) in both cases remains similar to parent frameworks due to lower uptakes at low pressures. In the case of NU-125, the effect of defects became more pronounced at lower temperatures, reflecting the greater surface areas and pore volumes of the altered forms.",
author = "Gokhan Barin and Vaiva Krungleviciute and Oleksii Gutov and Hupp, {Joseph T} and Taner Yildirim and Farha, {Omar K.}",
year = "2014",
month = "7",
day = "7",
doi = "10.1021/ic500722n",
language = "English",
volume = "53",
pages = "6914--6919",
journal = "Inorganic Chemistry",
issn = "0020-1669",
publisher = "American Chemical Society",
number = "13",

}

TY - JOUR

T1 - Defect creation by linker fragmentation in metal-organic frameworks and its effects on gas uptake properties

AU - Barin, Gokhan

AU - Krungleviciute, Vaiva

AU - Gutov, Oleksii

AU - Hupp, Joseph T

AU - Yildirim, Taner

AU - Farha, Omar K.

PY - 2014/7/7

Y1 - 2014/7/7

N2 - We successfully demonstrate an approach based on linker fragmentation to create defects and tune the pore volumes and surface areas of two metal-organic frameworks, NU-125 and HKUST-1, both of which feature copper paddlewheel nodes. Depending on the linker fragment composition, the defect can be either a vacant site or a functional group that the original linker does not have. In the first case, we show that both surface area and pore volume increase, while in the second case they decrease. The effect of defects on the high-pressure gas uptake is also studied over a large temperature and pressure range for different gases. We found that despite an increase in pore volume and surface area in structures with vacant sites, the absolute adsorption for methane decreases for HKUST-1 and slightly increases for NU-125. However, the working capacity (deliverable amount between 65 and 5 bar) in both cases remains similar to parent frameworks due to lower uptakes at low pressures. In the case of NU-125, the effect of defects became more pronounced at lower temperatures, reflecting the greater surface areas and pore volumes of the altered forms.

AB - We successfully demonstrate an approach based on linker fragmentation to create defects and tune the pore volumes and surface areas of two metal-organic frameworks, NU-125 and HKUST-1, both of which feature copper paddlewheel nodes. Depending on the linker fragment composition, the defect can be either a vacant site or a functional group that the original linker does not have. In the first case, we show that both surface area and pore volume increase, while in the second case they decrease. The effect of defects on the high-pressure gas uptake is also studied over a large temperature and pressure range for different gases. We found that despite an increase in pore volume and surface area in structures with vacant sites, the absolute adsorption for methane decreases for HKUST-1 and slightly increases for NU-125. However, the working capacity (deliverable amount between 65 and 5 bar) in both cases remains similar to parent frameworks due to lower uptakes at low pressures. In the case of NU-125, the effect of defects became more pronounced at lower temperatures, reflecting the greater surface areas and pore volumes of the altered forms.

UR - http://www.scopus.com/inward/record.url?scp=84903955512&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84903955512&partnerID=8YFLogxK

U2 - 10.1021/ic500722n

DO - 10.1021/ic500722n

M3 - Article

VL - 53

SP - 6914

EP - 6919

JO - Inorganic Chemistry

JF - Inorganic Chemistry

SN - 0020-1669

IS - 13

ER -