Electrical impedance spectra to monitor damage during tensile loading of cement composites

Alva Peled, Josep M. Torrents, Thomas O Mason, Surendra P. Shah, Edward J. Garboczi

Research output: Contribution to journalArticle

58 Citations (Scopus)

Abstract

Conductive fibers can reinforce concrete and monitor damage leading to the development of smart material. This work studied the correlation between the electrical (DC and AC) and mechanical properties of cement composites reinforced with conductive carbon fibers. The tensile behavior and impedance behavior of extruded and notched composites with a fiber volume fraction of 0.5 and 3% were examined; mechanical load and electrical field were applied longitudinally (in the direction of extrusion). The crack growth of these composites during loading was observed and analyzed by digital image correlation (DIC). A good correlation between the electrical and mechanical properties was found, in that when a sudden growth in the crack was observed, a dramatic change was also noticed in the impedance values. Taking advantage of the special frequency-dependent electrical properties of conductive fiber-reinforced composites, impedance values measured during the fracture process were used to distinguish and calculate three different areas at the crack front: uncracked area, bridging area, and open area. The bridging area is the zone where the fibers bridge the propagating crack. A greater bridging area was found for the 0.5% fiber composite, compared to the 3% fiber composite. This can be explained based on differences in the final length of the carbon fibers in the two composites.

Original languageEnglish
Pages (from-to)313-322
Number of pages10
JournalACI Materials Journal
Volume98
Issue number4
Publication statusPublished - Jul 2001

Fingerprint

Acoustic impedance
Cements
Composite materials
Fibers
Cracks
Carbon fibers
Electric properties
Mechanical properties
Intelligent materials
Extrusion
Crack propagation
Volume fraction
Concretes

Keywords

  • Carbon fibers
  • Cement
  • Composite
  • Electrical properties
  • Impedance spectroscopy

ASJC Scopus subject areas

  • Building and Construction
  • Materials Science(all)

Cite this

Peled, A., Torrents, J. M., Mason, T. O., Shah, S. P., & Garboczi, E. J. (2001). Electrical impedance spectra to monitor damage during tensile loading of cement composites. ACI Materials Journal, 98(4), 313-322.

Electrical impedance spectra to monitor damage during tensile loading of cement composites. / Peled, Alva; Torrents, Josep M.; Mason, Thomas O; Shah, Surendra P.; Garboczi, Edward J.

In: ACI Materials Journal, Vol. 98, No. 4, 07.2001, p. 313-322.

Research output: Contribution to journalArticle

Peled, A, Torrents, JM, Mason, TO, Shah, SP & Garboczi, EJ 2001, 'Electrical impedance spectra to monitor damage during tensile loading of cement composites', ACI Materials Journal, vol. 98, no. 4, pp. 313-322.
Peled, Alva ; Torrents, Josep M. ; Mason, Thomas O ; Shah, Surendra P. ; Garboczi, Edward J. / Electrical impedance spectra to monitor damage during tensile loading of cement composites. In: ACI Materials Journal. 2001 ; Vol. 98, No. 4. pp. 313-322.
@article{13113e390fc94e6d9b3b98dfed470247,
title = "Electrical impedance spectra to monitor damage during tensile loading of cement composites",
abstract = "Conductive fibers can reinforce concrete and monitor damage leading to the development of smart material. This work studied the correlation between the electrical (DC and AC) and mechanical properties of cement composites reinforced with conductive carbon fibers. The tensile behavior and impedance behavior of extruded and notched composites with a fiber volume fraction of 0.5 and 3{\%} were examined; mechanical load and electrical field were applied longitudinally (in the direction of extrusion). The crack growth of these composites during loading was observed and analyzed by digital image correlation (DIC). A good correlation between the electrical and mechanical properties was found, in that when a sudden growth in the crack was observed, a dramatic change was also noticed in the impedance values. Taking advantage of the special frequency-dependent electrical properties of conductive fiber-reinforced composites, impedance values measured during the fracture process were used to distinguish and calculate three different areas at the crack front: uncracked area, bridging area, and open area. The bridging area is the zone where the fibers bridge the propagating crack. A greater bridging area was found for the 0.5{\%} fiber composite, compared to the 3{\%} fiber composite. This can be explained based on differences in the final length of the carbon fibers in the two composites.",
keywords = "Carbon fibers, Cement, Composite, Electrical properties, Impedance spectroscopy",
author = "Alva Peled and Torrents, {Josep M.} and Mason, {Thomas O} and Shah, {Surendra P.} and Garboczi, {Edward J.}",
year = "2001",
month = "7",
language = "English",
volume = "98",
pages = "313--322",
journal = "ACI Materials Journal",
issn = "0889-325X",
publisher = "American Concrete Institute",
number = "4",

}

TY - JOUR

T1 - Electrical impedance spectra to monitor damage during tensile loading of cement composites

AU - Peled, Alva

AU - Torrents, Josep M.

AU - Mason, Thomas O

AU - Shah, Surendra P.

AU - Garboczi, Edward J.

PY - 2001/7

Y1 - 2001/7

N2 - Conductive fibers can reinforce concrete and monitor damage leading to the development of smart material. This work studied the correlation between the electrical (DC and AC) and mechanical properties of cement composites reinforced with conductive carbon fibers. The tensile behavior and impedance behavior of extruded and notched composites with a fiber volume fraction of 0.5 and 3% were examined; mechanical load and electrical field were applied longitudinally (in the direction of extrusion). The crack growth of these composites during loading was observed and analyzed by digital image correlation (DIC). A good correlation between the electrical and mechanical properties was found, in that when a sudden growth in the crack was observed, a dramatic change was also noticed in the impedance values. Taking advantage of the special frequency-dependent electrical properties of conductive fiber-reinforced composites, impedance values measured during the fracture process were used to distinguish and calculate three different areas at the crack front: uncracked area, bridging area, and open area. The bridging area is the zone where the fibers bridge the propagating crack. A greater bridging area was found for the 0.5% fiber composite, compared to the 3% fiber composite. This can be explained based on differences in the final length of the carbon fibers in the two composites.

AB - Conductive fibers can reinforce concrete and monitor damage leading to the development of smart material. This work studied the correlation between the electrical (DC and AC) and mechanical properties of cement composites reinforced with conductive carbon fibers. The tensile behavior and impedance behavior of extruded and notched composites with a fiber volume fraction of 0.5 and 3% were examined; mechanical load and electrical field were applied longitudinally (in the direction of extrusion). The crack growth of these composites during loading was observed and analyzed by digital image correlation (DIC). A good correlation between the electrical and mechanical properties was found, in that when a sudden growth in the crack was observed, a dramatic change was also noticed in the impedance values. Taking advantage of the special frequency-dependent electrical properties of conductive fiber-reinforced composites, impedance values measured during the fracture process were used to distinguish and calculate three different areas at the crack front: uncracked area, bridging area, and open area. The bridging area is the zone where the fibers bridge the propagating crack. A greater bridging area was found for the 0.5% fiber composite, compared to the 3% fiber composite. This can be explained based on differences in the final length of the carbon fibers in the two composites.

KW - Carbon fibers

KW - Cement

KW - Composite

KW - Electrical properties

KW - Impedance spectroscopy

UR - http://www.scopus.com/inward/record.url?scp=0035412988&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0035412988&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:0035412988

VL - 98

SP - 313

EP - 322

JO - ACI Materials Journal

JF - ACI Materials Journal

SN - 0889-325X

IS - 4

ER -