Enhanced stability of silicon for photoelectrochemical water oxidation through self-healing enabled by an alkaline protective electrolyte

Harold J. Fu, Ivan A. Moreno-Hernandez, Pakpoom Buabthong, Kimberly M. Papadantonakis, Bruce S. Brunschwig, Nathan S. Lewis

Research output: Contribution to journalArticlepeer-review

Abstract

Alkaline electrolytes impede the corrosion of Si photoanodes under positive potentials and/or illumination, due to the formation of a SiOx layer that etches 2-3 orders of magnitude more slowly than Si. Hence during water oxidation under illumination, pinholes in protection layers on Si photoanodes result in the local formation of a protective, stabilizing passive oxide on the Si surface. However, operation under natural diurnal insolation cycles additionally requires protection strategies that minimize the dark corrosive etching rate of Si at pinholes. We show herein that addition of [Fe(CN)6]3- to 1.0 M KOH(aq) results in a self-healing process that extends the lifetime to >280 h of an np+-Si(100) photoanode patterned with an array of Ni catalyst islands operated under simulated day/night cycles. The self-healing [Fe(CN)6]3- additive caused the exposed Si(100) surface to etch >180 times slower than the Si etch rate in 1.0 M KOH(aq) alone. No appreciable difference in etch rate or facet preference was observed between Si(100) and Si(111) surfaces in 1.0 M KOH(aq) with [Fe(CN)6]3-, indicating that the surface conformally oxidized before Si dissolved. The presence of [Fe(CN)6]3- minimally impacted the faradaic efficiency or overpotential of p+-Si/Ni electrodes for the oxygen-evolution reaction.

Original languageEnglish
Pages (from-to)4132-4141
Number of pages10
JournalEnergy and Environmental Science
Volume13
Issue number11
DOIs
Publication statusPublished - Nov 2020

ASJC Scopus subject areas

  • Environmental Chemistry
  • Renewable Energy, Sustainability and the Environment
  • Nuclear Energy and Engineering
  • Pollution

Fingerprint Dive into the research topics of 'Enhanced stability of silicon for photoelectrochemical water oxidation through self-healing enabled by an alkaline protective electrolyte'. Together they form a unique fingerprint.

Cite this