Abstract
Synthesis of uniform nanobelts of [ZnSe] (diethylenetriamine) 0.5 using a ternary solution composed of DETA, hydrazine hydrate, and deionized water was investigated. ZnSO4·7H2O and Na2SeO3 were added into solution under stirring. TEM images were acquired at an acceleration voltage of a 200 kV. Results show that the photoluminescence spectra change as the volume ratio of the ternary solution system is varied.
| Original language | English |
|---|---|
| Pages (from-to) | 2799-2802 |
| Number of pages | 4 |
| Journal | Advanced Materials |
| Volume | 17 |
| Issue number | 23 |
| DOIs | |
| Publication status | Published - Dec 5 2005 |
Fingerprint
ASJC Scopus subject areas
- Materials Science(all)
Cite this
Nanocrystals of an inorganic-organic hybrid semiconductor : Formation of uniform nanobelts of [ZnSe](diethylenetriamine)0.5 in a ternary solution. / Yao, Weitang; Yu, Shu Hong; Huang, Xiaoying; Jiang, Jun; Zhao, Lucy Q.; Pan, Long; Li, Jing.
In: Advanced Materials, Vol. 17, No. 23, 05.12.2005, p. 2799-2802.Research output: Contribution to journal › Article
}
TY - JOUR
T1 - Nanocrystals of an inorganic-organic hybrid semiconductor
T2 - Formation of uniform nanobelts of [ZnSe](diethylenetriamine)0.5 in a ternary solution
AU - Yao, Weitang
AU - Yu, Shu Hong
AU - Huang, Xiaoying
AU - Jiang, Jun
AU - Zhao, Lucy Q.
AU - Pan, Long
AU - Li, Jing
PY - 2005/12/5
Y1 - 2005/12/5
N2 - Synthesis of uniform nanobelts of [ZnSe] (diethylenetriamine) 0.5 using a ternary solution composed of DETA, hydrazine hydrate, and deionized water was investigated. ZnSO4·7H2O and Na2SeO3 were added into solution under stirring. TEM images were acquired at an acceleration voltage of a 200 kV. Results show that the photoluminescence spectra change as the volume ratio of the ternary solution system is varied.
AB - Synthesis of uniform nanobelts of [ZnSe] (diethylenetriamine) 0.5 using a ternary solution composed of DETA, hydrazine hydrate, and deionized water was investigated. ZnSO4·7H2O and Na2SeO3 were added into solution under stirring. TEM images were acquired at an acceleration voltage of a 200 kV. Results show that the photoluminescence spectra change as the volume ratio of the ternary solution system is varied.
UR - http://www.scopus.com/inward/record.url?scp=29144494521&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=29144494521&partnerID=8YFLogxK
U2 - 10.1002/adma.200501343
DO - 10.1002/adma.200501343
M3 - Article
VL - 17
SP - 2799
EP - 2802
JO - Advanced Materials
JF - Advanced Materials
SN - 0935-9648
IS - 23
ER -