Photoinjection of High Potential Holes into Cu5Ta11O30 Nanoparticles by Porphyrin Dyes

Ian Sullivan, Chelsea L. Brown, Manuel J. Llansola-Portoles, Miguel Gervaldo, Gerdenis Kodis, Thomas A. Moore, Devens Gust, Ana L. Moore, Paul A. Maggard

Research output: Contribution to journalArticle

7 Citations (Scopus)

Abstract

Excited-state hole injection into the valence band of Cu5Ta11O30 nanoparticles (NP-Cu5Ta11O30) was investigated through sensitization with zinc porphyrin dyes using simulated solar irradiance. The Cu5Ta11O30 nanoparticles were prepared by a flux-mediated synthesis and found to have an average particle size of ∼10-15 nm by DLS and TEM. The zinc 4-(10,15,20-tris(4-pyridinyl)-porphin-5-yl)phenylphosphonic acid (D1) and its analogue, in which the pyridine groups are methylated (D2), were synthesized and found to have excited-state reduction potentials appropriate for p-type dye sensitization of the nanoparticles. The dye-sensitized NP-Cu5Ta11O30 exhibited fluorescence quenching consistent with electron transfer from the NP-Cu5Ta11O30 to the dye; forward and recombination rates were obtained by transient absorption measurements. Hole injection times of 8 ps and <100 fs were observed for D1 and D2, respectively. Nanoparticulate films of Cu5Ta11O30 were prepared and evaluated in dye-sensitized solar cells under simulated solar irradiance (AM 1.5 G, 100 mW/cm2). Measurable photocurrents and open-circuit potentials (Voc) of 200 and 110 mV were observed using D1 and D2, respectively.

Original languageEnglish
Pages (from-to)21294-21303
Number of pages10
JournalJournal of Physical Chemistry C
Volume119
Issue number37
DOIs
Publication statusPublished - Sep 17 2015

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Energy(all)
  • Physical and Theoretical Chemistry
  • Surfaces, Coatings and Films

Fingerprint Dive into the research topics of 'Photoinjection of High Potential Holes into Cu<sub>5</sub>Ta<sub>11</sub>O<sub>30</sub> Nanoparticles by Porphyrin Dyes'. Together they form a unique fingerprint.

  • Cite this

    Sullivan, I., Brown, C. L., Llansola-Portoles, M. J., Gervaldo, M., Kodis, G., Moore, T. A., Gust, D., Moore, A. L., & Maggard, P. A. (2015). Photoinjection of High Potential Holes into Cu5Ta11O30 Nanoparticles by Porphyrin Dyes. Journal of Physical Chemistry C, 119(37), 21294-21303. https://doi.org/10.1021/acs.jpcc.5b02174