Remnant PbI2, an unforeseen necessity in high-efficiency hybrid perovskite-based solar cells?

Duyen H. Cao, Constantinos C. Stoumpos, Christos D. Malliakas, Michael J. Katz, Omar K. Farha, Joseph T Hupp, Mercouri G Kanatzidis

Research output: Contribution to journalArticle

176 Citations (Scopus)

Abstract

Perovskite-containing solar cells were fabricated in a two-step procedure in which PbI2is deposited via spin-coating and subsequently converted to the CH3NH3PbI3perovskite by dipping in a solution of CH3NH3I. By varying the dipping time from 5 s to 2 h, we observe that the device performance shows an unexpectedly remarkable trend. At dipping times below 15 min the current density and voltage of the device are enhanced from 10.1 mA/cm2and 933 mV (5 s) to 15.1 mA/cm2and 1036 mV (15 min). However, upon further conversion, the current density decreases to 9.7 mA/cm2and 846 mV after 2 h. Based on X-ray diffraction data, we determined that remnant PbI2is always present in these devices. Work function and dark current measurements showed that the remnant PbI2has a beneficial effect and acts as a blocking layer between the TiO2semiconductor and the perovskite itself reducing the probability of back electron transfer (charge recombination). Furthermore, we find that increased dipping time leads to an increase in the size of perovskite crystals at the perovskite-hole-transporting material interface. Overall, approximately 15 min dipping time (∼ 2% unconverted PbI2) is necessary for achieving optimal device efficiency.

Original languageEnglish
Article number091101
JournalAPL Materials
Volume2
Issue number9
DOIs
Publication statusPublished - 2014

Fingerprint

Perovskite
Solar cells
Current density
Dark currents
Spin coating
Electric current measurement
Charge transfer
X ray diffraction
Crystals
perovskite
Electrons
Electric potential

ASJC Scopus subject areas

  • Materials Science(all)
  • Engineering(all)

Cite this

Remnant PbI2, an unforeseen necessity in high-efficiency hybrid perovskite-based solar cells? / Cao, Duyen H.; Stoumpos, Constantinos C.; Malliakas, Christos D.; Katz, Michael J.; Farha, Omar K.; Hupp, Joseph T; Kanatzidis, Mercouri G.

In: APL Materials, Vol. 2, No. 9, 091101, 2014.

Research output: Contribution to journalArticle

Cao, Duyen H. ; Stoumpos, Constantinos C. ; Malliakas, Christos D. ; Katz, Michael J. ; Farha, Omar K. ; Hupp, Joseph T ; Kanatzidis, Mercouri G. / Remnant PbI2, an unforeseen necessity in high-efficiency hybrid perovskite-based solar cells?. In: APL Materials. 2014 ; Vol. 2, No. 9.
@article{bafd36d5cbac444fb85c11a3acc34204,
title = "Remnant PbI2, an unforeseen necessity in high-efficiency hybrid perovskite-based solar cells?",
abstract = "Perovskite-containing solar cells were fabricated in a two-step procedure in which PbI2is deposited via spin-coating and subsequently converted to the CH3NH3PbI3perovskite by dipping in a solution of CH3NH3I. By varying the dipping time from 5 s to 2 h, we observe that the device performance shows an unexpectedly remarkable trend. At dipping times below 15 min the current density and voltage of the device are enhanced from 10.1 mA/cm2and 933 mV (5 s) to 15.1 mA/cm2and 1036 mV (15 min). However, upon further conversion, the current density decreases to 9.7 mA/cm2and 846 mV after 2 h. Based on X-ray diffraction data, we determined that remnant PbI2is always present in these devices. Work function and dark current measurements showed that the remnant PbI2has a beneficial effect and acts as a blocking layer between the TiO2semiconductor and the perovskite itself reducing the probability of back electron transfer (charge recombination). Furthermore, we find that increased dipping time leads to an increase in the size of perovskite crystals at the perovskite-hole-transporting material interface. Overall, approximately 15 min dipping time (∼ 2{\%} unconverted PbI2) is necessary for achieving optimal device efficiency.",
author = "Cao, {Duyen H.} and Stoumpos, {Constantinos C.} and Malliakas, {Christos D.} and Katz, {Michael J.} and Farha, {Omar K.} and Hupp, {Joseph T} and Kanatzidis, {Mercouri G}",
year = "2014",
doi = "10.1063/1.4895038",
language = "English",
volume = "2",
journal = "APL Materials",
issn = "2166-532X",
publisher = "American Institute of Physics Publising LLC",
number = "9",

}

TY - JOUR

T1 - Remnant PbI2, an unforeseen necessity in high-efficiency hybrid perovskite-based solar cells?

AU - Cao, Duyen H.

AU - Stoumpos, Constantinos C.

AU - Malliakas, Christos D.

AU - Katz, Michael J.

AU - Farha, Omar K.

AU - Hupp, Joseph T

AU - Kanatzidis, Mercouri G

PY - 2014

Y1 - 2014

N2 - Perovskite-containing solar cells were fabricated in a two-step procedure in which PbI2is deposited via spin-coating and subsequently converted to the CH3NH3PbI3perovskite by dipping in a solution of CH3NH3I. By varying the dipping time from 5 s to 2 h, we observe that the device performance shows an unexpectedly remarkable trend. At dipping times below 15 min the current density and voltage of the device are enhanced from 10.1 mA/cm2and 933 mV (5 s) to 15.1 mA/cm2and 1036 mV (15 min). However, upon further conversion, the current density decreases to 9.7 mA/cm2and 846 mV after 2 h. Based on X-ray diffraction data, we determined that remnant PbI2is always present in these devices. Work function and dark current measurements showed that the remnant PbI2has a beneficial effect and acts as a blocking layer between the TiO2semiconductor and the perovskite itself reducing the probability of back electron transfer (charge recombination). Furthermore, we find that increased dipping time leads to an increase in the size of perovskite crystals at the perovskite-hole-transporting material interface. Overall, approximately 15 min dipping time (∼ 2% unconverted PbI2) is necessary for achieving optimal device efficiency.

AB - Perovskite-containing solar cells were fabricated in a two-step procedure in which PbI2is deposited via spin-coating and subsequently converted to the CH3NH3PbI3perovskite by dipping in a solution of CH3NH3I. By varying the dipping time from 5 s to 2 h, we observe that the device performance shows an unexpectedly remarkable trend. At dipping times below 15 min the current density and voltage of the device are enhanced from 10.1 mA/cm2and 933 mV (5 s) to 15.1 mA/cm2and 1036 mV (15 min). However, upon further conversion, the current density decreases to 9.7 mA/cm2and 846 mV after 2 h. Based on X-ray diffraction data, we determined that remnant PbI2is always present in these devices. Work function and dark current measurements showed that the remnant PbI2has a beneficial effect and acts as a blocking layer between the TiO2semiconductor and the perovskite itself reducing the probability of back electron transfer (charge recombination). Furthermore, we find that increased dipping time leads to an increase in the size of perovskite crystals at the perovskite-hole-transporting material interface. Overall, approximately 15 min dipping time (∼ 2% unconverted PbI2) is necessary for achieving optimal device efficiency.

UR - http://www.scopus.com/inward/record.url?scp=84907262102&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84907262102&partnerID=8YFLogxK

U2 - 10.1063/1.4895038

DO - 10.1063/1.4895038

M3 - Article

AN - SCOPUS:84907262102

VL - 2

JO - APL Materials

JF - APL Materials

SN - 2166-532X

IS - 9

M1 - 091101

ER -