Thin Films and Solar Cells Based on Semiconducting Two-Dimensional Ruddlesden-Popper (CH3(CH2)3NH3)2(CH3NH3)n-1SnnI3n+1 Perovskites

Duyen H. Cao, Constantinos C. Stoumpos, Takamichi Yokoyama, Jenna L. Logsdon, Tze Bin Song, Omar K. Farha, Michael R Wasielewski, Joseph T Hupp, Mercouri G Kanatzidis

Research output: Contribution to journalArticle

89 Citations (Scopus)

Abstract

Low electrical resistivity (high dark carrier concentration) of CH3NH3SnI3 often leads to short-circuiting in solar cells, and appropriate thin-film modifications are required to ensure functional devices. The long-term durability of organic-inorganic perovskite solar cells necessitates the protection of perovskite thin films from moisture to prevent material decomposition. Herein, we report that the electrical resistivity and the moisture stability of two-dimensional (2D) Ruddlesden-Popper (CH3(CH2)3NH3)2(CH3NH3)n-1SnnI3n+1 perovskites are considerably improved compared to those of the three-dimensional (3D) CH3NH3SnI3 perovskite and subsequently show the solar cell fabrication using a simple one-step spin-coating method. These 2D perovskites are semiconductors with optical band gaps progressively decreasing from 1.83 eV (n = 1) to 1.20 eV (n = ). The n = 3 and n = 4 members with optimal band gaps of 1.50 and 1.42 eV for solar cells, respectively, were thus chosen for in-depth studies. We demonstrate that thin films of 2D perovskites orient the {(CH3NH3)n-1SnnI3n+1}2- slabs parallel to the substrate when dimethyl sulfoxide solvent is used for deposition, and this orientation can be flipped to perpendicular when N,N-dimethylformamide solvent is used. We find that high-purity, single-phase films can be grown only by using precursor solutions of "pre-synthesized" single-phase bulk perovskite materials. We introduce for the first time the use of triethylphosphine as an effective antioxidant, which suppresses the doping level of the 2D films and improves film morphology. The resulting semiconducting 2D Sn-based iodide perovskite films were incorporated in solar cells yielding a power conversion efficiency of 2.5% from the Sn4I13 member. From the temporal stability standpoint, the 2D Sn perovskite solar cells outperform their 3D analogs.

Original languageEnglish
Pages (from-to)982-990
Number of pages9
JournalACS Energy Letters
Volume2
Issue number5
DOIs
Publication statusPublished - May 12 2017

Fingerprint

Perovskite
Solar cells
Thin films
Moisture
Dimethylformamide
Dimethyl sulfoxide
Optical band gaps
Spin coating
Iodides
Dimethyl Sulfoxide
Antioxidants
Conversion efficiency
Carrier concentration
Durability
Energy gap
Doping (additives)
Semiconductor materials
Decomposition
Fabrication
perovskite

ASJC Scopus subject areas

  • Chemistry (miscellaneous)
  • Renewable Energy, Sustainability and the Environment
  • Fuel Technology
  • Energy Engineering and Power Technology
  • Materials Chemistry

Cite this

Thin Films and Solar Cells Based on Semiconducting Two-Dimensional Ruddlesden-Popper (CH3(CH2)3NH3)2(CH3NH3)n-1SnnI3n+1 Perovskites. / Cao, Duyen H.; Stoumpos, Constantinos C.; Yokoyama, Takamichi; Logsdon, Jenna L.; Song, Tze Bin; Farha, Omar K.; Wasielewski, Michael R; Hupp, Joseph T; Kanatzidis, Mercouri G.

In: ACS Energy Letters, Vol. 2, No. 5, 12.05.2017, p. 982-990.

Research output: Contribution to journalArticle

Cao, Duyen H. ; Stoumpos, Constantinos C. ; Yokoyama, Takamichi ; Logsdon, Jenna L. ; Song, Tze Bin ; Farha, Omar K. ; Wasielewski, Michael R ; Hupp, Joseph T ; Kanatzidis, Mercouri G. / Thin Films and Solar Cells Based on Semiconducting Two-Dimensional Ruddlesden-Popper (CH3(CH2)3NH3)2(CH3NH3)n-1SnnI3n+1 Perovskites. In: ACS Energy Letters. 2017 ; Vol. 2, No. 5. pp. 982-990.
@article{1d0b4de63ed749a8bcee0ed56dfe7d98,
title = "Thin Films and Solar Cells Based on Semiconducting Two-Dimensional Ruddlesden-Popper (CH3(CH2)3NH3)2(CH3NH3)n-1SnnI3n+1 Perovskites",
abstract = "Low electrical resistivity (high dark carrier concentration) of CH3NH3SnI3 often leads to short-circuiting in solar cells, and appropriate thin-film modifications are required to ensure functional devices. The long-term durability of organic-inorganic perovskite solar cells necessitates the protection of perovskite thin films from moisture to prevent material decomposition. Herein, we report that the electrical resistivity and the moisture stability of two-dimensional (2D) Ruddlesden-Popper (CH3(CH2)3NH3)2(CH3NH3)n-1SnnI3n+1 perovskites are considerably improved compared to those of the three-dimensional (3D) CH3NH3SnI3 perovskite and subsequently show the solar cell fabrication using a simple one-step spin-coating method. These 2D perovskites are semiconductors with optical band gaps progressively decreasing from 1.83 eV (n = 1) to 1.20 eV (n = ). The n = 3 and n = 4 members with optimal band gaps of 1.50 and 1.42 eV for solar cells, respectively, were thus chosen for in-depth studies. We demonstrate that thin films of 2D perovskites orient the {(CH3NH3)n-1SnnI3n+1}2- slabs parallel to the substrate when dimethyl sulfoxide solvent is used for deposition, and this orientation can be flipped to perpendicular when N,N-dimethylformamide solvent is used. We find that high-purity, single-phase films can be grown only by using precursor solutions of {"}pre-synthesized{"} single-phase bulk perovskite materials. We introduce for the first time the use of triethylphosphine as an effective antioxidant, which suppresses the doping level of the 2D films and improves film morphology. The resulting semiconducting 2D Sn-based iodide perovskite films were incorporated in solar cells yielding a power conversion efficiency of 2.5{\%} from the Sn4I13 member. From the temporal stability standpoint, the 2D Sn perovskite solar cells outperform their 3D analogs.",
author = "Cao, {Duyen H.} and Stoumpos, {Constantinos C.} and Takamichi Yokoyama and Logsdon, {Jenna L.} and Song, {Tze Bin} and Farha, {Omar K.} and Wasielewski, {Michael R} and Hupp, {Joseph T} and Kanatzidis, {Mercouri G}",
year = "2017",
month = "5",
day = "12",
doi = "10.1021/acsenergylett.7b00202",
language = "English",
volume = "2",
pages = "982--990",
journal = "ACS Energy Letters",
issn = "2380-8195",
publisher = "American Chemical Society",
number = "5",

}

TY - JOUR

T1 - Thin Films and Solar Cells Based on Semiconducting Two-Dimensional Ruddlesden-Popper (CH3(CH2)3NH3)2(CH3NH3)n-1SnnI3n+1 Perovskites

AU - Cao, Duyen H.

AU - Stoumpos, Constantinos C.

AU - Yokoyama, Takamichi

AU - Logsdon, Jenna L.

AU - Song, Tze Bin

AU - Farha, Omar K.

AU - Wasielewski, Michael R

AU - Hupp, Joseph T

AU - Kanatzidis, Mercouri G

PY - 2017/5/12

Y1 - 2017/5/12

N2 - Low electrical resistivity (high dark carrier concentration) of CH3NH3SnI3 often leads to short-circuiting in solar cells, and appropriate thin-film modifications are required to ensure functional devices. The long-term durability of organic-inorganic perovskite solar cells necessitates the protection of perovskite thin films from moisture to prevent material decomposition. Herein, we report that the electrical resistivity and the moisture stability of two-dimensional (2D) Ruddlesden-Popper (CH3(CH2)3NH3)2(CH3NH3)n-1SnnI3n+1 perovskites are considerably improved compared to those of the three-dimensional (3D) CH3NH3SnI3 perovskite and subsequently show the solar cell fabrication using a simple one-step spin-coating method. These 2D perovskites are semiconductors with optical band gaps progressively decreasing from 1.83 eV (n = 1) to 1.20 eV (n = ). The n = 3 and n = 4 members with optimal band gaps of 1.50 and 1.42 eV for solar cells, respectively, were thus chosen for in-depth studies. We demonstrate that thin films of 2D perovskites orient the {(CH3NH3)n-1SnnI3n+1}2- slabs parallel to the substrate when dimethyl sulfoxide solvent is used for deposition, and this orientation can be flipped to perpendicular when N,N-dimethylformamide solvent is used. We find that high-purity, single-phase films can be grown only by using precursor solutions of "pre-synthesized" single-phase bulk perovskite materials. We introduce for the first time the use of triethylphosphine as an effective antioxidant, which suppresses the doping level of the 2D films and improves film morphology. The resulting semiconducting 2D Sn-based iodide perovskite films were incorporated in solar cells yielding a power conversion efficiency of 2.5% from the Sn4I13 member. From the temporal stability standpoint, the 2D Sn perovskite solar cells outperform their 3D analogs.

AB - Low electrical resistivity (high dark carrier concentration) of CH3NH3SnI3 often leads to short-circuiting in solar cells, and appropriate thin-film modifications are required to ensure functional devices. The long-term durability of organic-inorganic perovskite solar cells necessitates the protection of perovskite thin films from moisture to prevent material decomposition. Herein, we report that the electrical resistivity and the moisture stability of two-dimensional (2D) Ruddlesden-Popper (CH3(CH2)3NH3)2(CH3NH3)n-1SnnI3n+1 perovskites are considerably improved compared to those of the three-dimensional (3D) CH3NH3SnI3 perovskite and subsequently show the solar cell fabrication using a simple one-step spin-coating method. These 2D perovskites are semiconductors with optical band gaps progressively decreasing from 1.83 eV (n = 1) to 1.20 eV (n = ). The n = 3 and n = 4 members with optimal band gaps of 1.50 and 1.42 eV for solar cells, respectively, were thus chosen for in-depth studies. We demonstrate that thin films of 2D perovskites orient the {(CH3NH3)n-1SnnI3n+1}2- slabs parallel to the substrate when dimethyl sulfoxide solvent is used for deposition, and this orientation can be flipped to perpendicular when N,N-dimethylformamide solvent is used. We find that high-purity, single-phase films can be grown only by using precursor solutions of "pre-synthesized" single-phase bulk perovskite materials. We introduce for the first time the use of triethylphosphine as an effective antioxidant, which suppresses the doping level of the 2D films and improves film morphology. The resulting semiconducting 2D Sn-based iodide perovskite films were incorporated in solar cells yielding a power conversion efficiency of 2.5% from the Sn4I13 member. From the temporal stability standpoint, the 2D Sn perovskite solar cells outperform their 3D analogs.

UR - http://www.scopus.com/inward/record.url?scp=85021823998&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85021823998&partnerID=8YFLogxK

U2 - 10.1021/acsenergylett.7b00202

DO - 10.1021/acsenergylett.7b00202

M3 - Article

VL - 2

SP - 982

EP - 990

JO - ACS Energy Letters

JF - ACS Energy Letters

SN - 2380-8195

IS - 5

ER -