Three-Dimensional Lead Iodide Perovskitoid Hybrids with High X-ray Photoresponse

Xiaotong Li, Yihui He, Mikaël Kepenekian, Peijun Guo, Weijun Ke, Jacky Even, Claudine Katan, Constantinos C. Stoumpos, Richard D. Schaller, Mercouri G. Kanatzidis

Research output: Contribution to journalArticle

Abstract

Large organic A cations cannot stabilize the 3D perovskite AMX3 structure because they cannot be accommodated in the cubo-octhedral cage (do not follow the Goldschmidt tolerance factor rule), and they generally template low-dimensional structures. Here we report that the large dication aminomethylpyridinium (AMPY) can template novel 3D structures which resemble conventional perovskites. They have the formula (xAMPY)M2I6 (x = 3 or 4, M = Sn2+ or Pb2+) which is double of the AMX3 formula. However, because of the steric requirement of the Goldschmidt tolerance factor rule, it is impossible for (xAMPY)M2I6 to form proper perovskite structures. Instead, a combination of corner-sharing and edge-sharing connectivity is adopted in these compounds leading to the new 3D structures. DFT calculations reveal that the compounds are indirect band gap semiconductors with direct band gaps presenting at slightly higher energies and dispersive electronic bands. The indirect band gaps of the Sn and Pb compounds are ∼1.7 and 2.0 eV, respectively, which is slightly higher than the corresponding AMI3 3D perovskites. The Raman spectra for the compounds are diffuse, with a broad rising central peak at very low frequencies around 0 cm-1, a feature that is characteristic of dynamical lattices, high anharmonicity, and dissipative vibrations very similar to the 3D AMX3 perovskites. Devices of (3AMPY)Pb2I6 crystals exhibit clear photoresponse under ambient light without applied bias, reflecting a high carrier mobility (μ) and long carrier lifetime (τ). The devices also exhibit sizable X-ray generated photocurrent with a high μτ product of ∼1.2 × 10-4 cm2 /V and an X-ray sensitivity of 207 μC·Gy-1·cm-2

Original languageEnglish
Pages (from-to)6625-6637
Number of pages13
JournalJournal of the American Chemical Society
Volume142
Issue number14
DOIs
Publication statusPublished - Apr 8 2020

    Fingerprint

ASJC Scopus subject areas

  • Catalysis
  • Chemistry(all)
  • Biochemistry
  • Colloid and Surface Chemistry

Cite this