YBa2Cu3O7-δ on MgO films grown by pulsed organometallic beam epitaxy and a grain boundary junction application

K. A. Dean, D. B. Buchholz, L. D. Marks, R. P.H. Chang, B. V. Vuchic, K. L. Merkle, D. B. Studebaker, T. J. Marks

Research output: Contribution to journalArticlepeer-review

11 Citations (Scopus)

Abstract

MgO films and YBa2Cu3O7-δ/MgO multilayer films were developed with the pulsed organometallic beam epitaxy (POMBE) growth technique, and grain boundary junctions were fabricated from the films to demonstrate the utility of the multilayers. High-quality MgO films were grown on LaA1O3 substrates by POMBE using a Mg(dpm)2 precursor. MgO crystallinity, as assessed by x-ray diffraction rocking curves, improved with the use of CuOx or YBa2Cu3O7-δ buffer layers. YBa2Cu3O7-δ films grown on the MgO layer by POMBE exhibited a Tc0of 83 K and a Jc(12 K) exceeding 106 A/cm2 for applied magnetic fields up to 3 × 104 G. Grain boundary junctions were formed by growing YBa2Cu3O7-δ on MgO films that had been pretreated with a simple sputtering technique. This sputtering induces a controlled, 45° grain boundary in subsequently deposited YBa2Cu3O7-δ films. The resulting boundary showed weak-link current-voltage behavior and an IcRnproduct of 52 μV at 10 K, demonstrating that sputter-induced grain boundary junctions are compatible with multilayer technology.

Original languageEnglish
Pages (from-to)2700-2707
Number of pages8
JournalJournal of Materials Research
Volume10
Issue number11
DOIs
Publication statusPublished - Nov 1995

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7</sub>-<sub>δ</sub> on MgO films grown by pulsed organometallic beam epitaxy and a grain boundary junction application'. Together they form a unique fingerprint.

Cite this